Home > Monolithic Refractory > Refractory Castable

Refractory Castable

products +

Low Cement Castable

Low Cement Castable
1. Chemical component :≥ 65

2. Aggregate：Mullite & Corundum

3. Maximum service temperature：≥ 1600

4. Refractorinee:≥1750

5. Bulk density g/cm³：≥2.6

6. 1300℃Pressure strength after sintered:±0.5
High Alumina Castable

High Alumina Castable
High Alumina Castable is a kind of refractory castable which uses high alumina raw material as aggregates and the powder and then be added with binding agent. High aluminum refractory castable has high mechanical strength, good thermal shock resistance, good corrosion resistance. It's mainly used for furnace lining of boiler, blast furnace hot blast stove, heating furnace, ceramic kiln and various industrial furnaces.
Acid Resistant Castable

Acid Resistant Castable
1). High temperature resistance
2). High tensile strength
3). Acid erosion resistance
4). Great uniformity
5). Resistant to high humidity
6). High content of water and anchoring agent
7). High compression ratio
Lightweight Insulating Castable

Lightweight Insulating Castable
(1) Small bulk density and low thermal conductivity, reducing the structural weight of the furnace or equipment.
(2) Excellent heat insulation and heat insulation, making the temperature in the furnace uniform.
(3) An integral lining material of any shape that can be used in a good project.
(4) Strong spalling resistance.
(5) Chemical resistance to acid and alkaline gases.
(6) Good workability and high bond strength.
Corundum Mullite Castable

Corundum Mullite Castable
(1) The construction is convenient.
(2) High-strength explosion-proof.
(3) High temperature resistance and high operating temperature.
(4) Under 0.2mpa pressure, the softening temperature of the load is high.
(5) High temperature volume stability, high strength.
(6) Anti-slag slag has strong chemical corrosion.
(7) The overall structure is stable and resistant to spalling.
(8) Quenching and rapid heat resistance, excellent thermal shock resistance.
High Strength Abrasion Resistant Castable

High Strength Abrasion Resistant Castable
High temperature abrasion resistance;
High crushing strength;
High modulus of rupture;
Good slag corrosion resistance;
Scouring resistance;
Good volume stability.
$Refractory Castable$

Refractory Castable

Refractory Castable
Refractory castables are a mixture of refractory aggregates, powders, binders and admixtures, which can withstand high temperatures of 1500°C to 1800°C. They are widely used in industrial kilns, high-temperature equipment, pizza ovens, etc.
Steel Ladle Castable

Steel Ladle Castable
Long life;
High temperature resistance;
Shock resistance & High strength;
High stability;
Ideal Ladle Refractories;
Application: Steel ladle castable mainly used in large,medium and small ladle.
Blast Furnace Iron Trough Castable

Blast Furnace Iron Trough Castable
Different types of refractory materials can be used as per the types of iron troughs. Iron storing troughs in middle and large scale steel mills usually adopt Al-Si-C series castable. Iron trough and slag trough castable has high mechanical strength, corrosion resistance, good flowability, and can be quickly dried. Iron trough castable should also has excellent thermal shock resistance.
Corundum High Strength Wear Resistant Castable

Corundum High Strength Wear Resistant Castable
Corundum high strength wear resistant castable adopts corundum, mullite as main raw materials, ultra fine micro powder, composite binder and additives are added into raw materials. It features in high strength, good abrasion resistance and excellent thermal shock resistance.
Corundum mullite high strength anti-wearing castable

Corundum mullite high strength anti-wearing castable
1100℃ Cold Crushing Strength Mpa ≥ : 100
Linear Dimensional Change % ≤：-0.3
Maximum Service Temperature ℃：1550
0.2MPa Refractoriness Under Load ℃ :≥1450
Bulk density g/cm³：≥2.7
Thermal Shock Resistance(900℃, water-cooling) ≥:25
Alkali Proof Castable

Alkali Proof Castable
1.Long service life,
2.High strength,
3.Low bulk density,
4.High refractoriness.